New inorganic pigments based on PbO were synthesized as high-temperature environment-friendly inorganic pigments.
This work is focused on mixed oxides based on PbO which are doped by rare earth elements, i.e. compounds with formula Pb0.9Si0.05Ta0.05O2.
The pigments were prepared by the solid state reaction.
Their color properties were investigated depending on content of selected elements and calcination temperature.
All prepared pigments were applied into organic matrix and ceramic glaze.
The pigments were evaluated from the standpoint of their color properties and particle sizes.
結論として、〜を開発した＞In conclusion, we have developed a new method for preparing pure g-Fe2O3 nanoparticles directly by laser ablation of tiny iron wire at atmospheric pressure.
結論として、〜を合成した＞In conclusion, the single phase of the nano-sized a-Fe2O3 samples have been synthesized using a new hydrothermal method.
that以下が明らかになった＞It was found that the size and nature of the nanoparticle strongly depends on the pH, oxalic acid and CTAB concentrations.
〜は〜であることが分かった＞The crystallization behavior of alkoxide-derived amorphous oxides within the PZT system was found to depend strongly on both chemical composition and heat treatment temperature.
〜で発見した＞A suitable nonlead replacement of lead-based piezoelectrics can be found in the LN-NN-KN ternary system.
〜を評価した＞Three types of hybrid electrodes were evaluated as a replacement for the bottom RuO2 electrode in the capacitors.
〜はthat以下を示唆（示す）した。＞Changes in crystallization temperatures suggest that PbO acts as a modifier within the amorphous network, leading to fewer M-O-M bonds in PbO-excess compositions, which is kinetically more favorable for crystallization.
その結果はthat以下を示唆している。＞The results suggest that direct crystallization of perovskite from the amorphous precursor, i.e., without fluorine formation, may be more likely near PTO than PZT.
この論文は〜を比較している。＞This paper compares the temperature dependence of dielectric and piezoelectric properties for the MPB compositions in BNT-BKT and BNT-BT system along with that of KNN system.
that以下が明らかだった＞It was shown that using hybrid electrodes can result in PZT capacitors with leakage currents two to four orders of magnitude lower than those of a typical capacitor.
〜を成し遂げた＞This reduction in leakage current is achieved while at the same time maintaining the excellent resistance to the polarization fatigue characteristic of the capacitors.